Low alloy tool steel bar, DIN 86CrMoV7
Delivery term:The date of payment from buyers deliver within days- Price:
Negotiable
- minimum:
- Total supply:
- Delivery term:
The date of payment from buyers deliver within days
- seat:
Beijing
- Validity to:
Long-term effective
- Last update:
2017-12-08 01:29
- Browse the number:
170
Company Profile
- Shanghai Bozhong Metal Group Co. Ltd By certification [File Integrity]
-
Contact:
bozhong(Ms.)
- Telephone:
-
Area:
Beijing
-
Address:
BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website: http://bozhong.vintagechinahirehertford.com/
Product details
Model Number: ZXL121
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionLow alloyed cold working tool steel.ApplicationsCold rolls, back-up rolls, straightening rolls, non-ferrous-2 and 4 high roll mills.Chemical Composition (in weight%)C 0.87
Si 0.30
Mn 0.38
Cr 1.75
V 0.10
Mo 0.28
Ni 0.13
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m. K]: 35.0
Electric resistivity [Ohm mm2/m]: 0.30
Specific heat capacity [J/g. K]: 0.46
Soft Annealing
Heat to 720-750℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650℃, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden froma temperature of 800-820℃, 830-850℃followed by oilor water quenching. Hardness after quenching is 64-67HRC.
Tempering
Tempering temperature: 200-600℃
Forging
Hot forming temperature: 1150-850℃.
Specifications:
Grade: 86CrMoV7
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements.
Delivery: 7-20 days after received deposit of T/T.
Si 0.30
Mn 0.38
Cr 1.75
V 0.10
Mo 0.28
Ni 0.13
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.85
Thermal conductivity [W/m. K]: 35.0
Electric resistivity [Ohm mm2/m]: 0.30
Specific heat capacity [J/g. K]: 0.46
Soft Annealing
Heat to 720-750℃, cool slowly in furnace. This will produce a maximum Brinell hardness of 230.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650℃, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden froma temperature of 800-820℃, 830-850℃followed by oilor water quenching. Hardness after quenching is 64-67HRC.
Tempering
Tempering temperature: 200-600℃
Forging
Hot forming temperature: 1150-850℃.
Specifications:
Grade: 86CrMoV7
Standard: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements.
Delivery: 7-20 days after received deposit of T/T.
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
- Dimensions per Unit: 2 × 0.5 × 0.5 Meters
- Weight per Unit: 20 Kilograms
- Units per Export Carton: 5
- Export Carton Dimensions L/W/H: 2 × 0.5 × 0.5 Meters
- Export Carton Weight: 5 Tons (US)
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe
New Products
-
PL1500 Rock Drilling and Splitting Machine
price: Negotiable
-
Multi-Station Plastic Thermoforming Boxes Production Machines
price: Negotiable
-
5kw Off Grid Solar Energy System
price: Negotiable
-
Outdoor Rattan Scoop Chairs
price: Negotiable
-
12 Volt Tyre Air Compressor
price: Negotiable
-
Rattan Egg Chair Double
price: Negotiable